The method is principle to coating materials having lead contents in the range of about 0,01 % (m/m) to 2 % (m/m), may also be applicable to products with a total lead content of more than 2 % (m/m) when the requirements of precision does not exceed the specified values. two methods are given. The principle of the dry ashing method consists in evaporation of a test portion to dryness and ashing at 475 C and extraction of any lead in the residue with hydrochloric acid; that of the wet oxidation method consists in wet oxidation of a test portion with a mixture of sulfuric acid and hydrogen peroxide or with sulfuric acid and nitric acid and extraction of any lead in the residue with EDTA and ammonia solution.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 1984-10Этап: Систематический пересмотр между-народного стандарта [90.20]
-
Версия: 1
-
Технический комитет :ISO/TC 256ICS :87.040
- RSS обновления
Preview
Жизненный цикл
-
Сейчас
ОпубликованоISO 6503:1984
Стандарт, который пересматривается каждые 5 лет
Этап: 90.20 (Hа стадии пересмотра)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
Появились вопросы?
Ознакомьтесь с FAQ
Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)