ISO 9588:2007 specifies procedures for reducing susceptibility, or degree of susceptibility, to hydrogen embrittlement that can arise in surface finishing processes.
The heat-treatment procedures for iron or steel specified in ISO 9588:2007 have been shown to be effective in reducing the susceptibility to hydrogen embrittlement. These heat-treatment procedures are used after surface finishing, but prior to any secondary conversion-coating operation.
Stress-relief heat-treatment procedures applied after fabrication, but prior to surface finishing, are specified in ISO 9587.
ISO 9588:2007 does not apply to fasteners.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 2007-12Этап: Международный стандарт подлежит пересмотру [90.92]
-
Версия: 2
-
Технический комитет :ISO/TC 107/SC 3
- RSS обновления
Новая версия в процессе разработки
![](/modules/iso-jahia-service-module/img/iso-logo.png)
ISO/DIS 24251-1
ISO/DIS 24251-1
Prevention of hydrogen assisted brittle fracture of high-strength steel components
Part 1: Fundamentals and measures
Жизненный цикл
-
Ранее
ОтозваноISO 9588:1999
-
Сейчас
ОпубликованоISO 9588:2007
Стандарт, который пересматривается каждые 5 лет
Этап: 90.92 (Будет пересмотрено)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
-
Будет заменено
В стадии разработкиISO/DIS 24251-1
Появились вопросы?
Ознакомьтесь с FAQ
Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)